16″ OD Flare Line Rehabilitation with NRI’s composites

An NDT inspection revealed a high condensation of H2S gas had caused internal corrosion in several places in a petroleum company’s flare line. During the inspection corrosion was located all over the pipe, including complex geometries such as elbows and tees. In some places, the steel was so compromised by the corrosion, that ordinary means of surface prep would not even be possible. Take a look below to see how NRI’s engineers provided a customized solution.